Steel is made by the Bessemer, Siemens Open Hearth, basic oxygen furnace, electric arc, electric high-frequency and crucible processes.
Crucible and high-frequency methods
The Huntsman crucible process has been superseded by the high frequency induction furnace in which the heat is generated in the metal itself by eddy currents induced by a magnetic field set up by an alternating current, which passes round water-cooled coils surrounding the crucible. The eddy currents increase with the square of the frequency, and an input current which alternates from 500 to 2000 hertz is necessary. As the frequency increases, the eddy currents tend to travel nearer and nearer the surface of a charge (i.e. shallow penetration). The heat developed in the charge depends on the cross-sectional area which carries current, and large furnaces use frequencies low enough to get adequate current penetration.
Automatic circulation of the melt in a vertical direction, due to eddy currents, promotes uniformity of analysis. Contamination by furnace gases is obviated and charges from 1 to 5 tonnes can be melted with resultant economy. Consequently, these electric furnaces are being used to produce high quality steels, such as ball bearing, stainless, magnet, die and tool steels.
The Huntsman crucible process has been superseded by the high frequency induction furnace in which the heat is generated in the metal itself by eddy currents induced by a magnetic field set up by an alternating current, which passes round water-cooled coils surrounding the crucible. The eddy currents increase with the square of the frequency, and an input current which alternates from 500 to 2000 hertz is necessary. As the frequency increases, the eddy currents tend to travel nearer and nearer the surface of a charge (i.e. shallow penetration). The heat developed in the charge depends on the cross-sectional area which carries current, and large furnaces use frequencies low enough to get adequate current penetration.
Automatic circulation of the melt in a vertical direction, due to eddy currents, promotes uniformity of analysis. Contamination by furnace gases is obviated and charges from 1 to 5 tonnes can be melted with resultant economy. Consequently, these electric furnaces are being used to produce high quality steels, such as ball bearing, stainless, magnet, die and tool steels.
Acid and basic steels
The remaining methods for making steel do so by removing impurities from pig iron or a mixture of pig iron and steel scrap. The impurities removed, however, depend on whether an acid (siliceous) or basic (limey) slag is used. An acid slag necessitates the use of an acid furnace lining (silica); a basic slag, a basic lining of magnesite or dolomite, with line in the charge. With an acid slag silicon, manganese and carbon only are removed by oxidation, consequently the raw material must not contain phosphorus and sulphur in amounts exceeding those permissible in the finished steel.
In the basic processes, silicon, manganese, carbon, phosphorus and sulphur can be removed from the charge, but normally the raw material contains low silicon and high phosphorus contents. To remove the phosphorus the bath of metal must be oxidised to a greater extent than in the corresponding acid process, and the final quality of the steel depends very largely on the degree of this oxidation, before deoxidisers-ferro-manganese, ferro-silicon, aluminium-remove the soluble iron oxide and form other insoluble oxides, which produce non-metallic inclusions if they are not removed from the melt:
2Al + 3FeO (soluble) « 3Fe + Al2O3 (solid)
In the acid processes, deoxidation can take place in the furnaces, leaving a reasonable time for the inclusions to rise into the slag and so be removed before casting. Whereas in the basic furnaces, deoxidation is rarely carried out in the presence of the slag, otherwise phosphorus would return to the metal. Deoxidation of the metal frequently takes place in the ladle, leaving only a short time for the deoxidation products to be removed. For these reasons acid steel is considered better than basic for certain purposes, such as large forging ingots and ball bearing steel. The introduction of vacuum degassing hastened the decline of the acid processes.
The remaining methods for making steel do so by removing impurities from pig iron or a mixture of pig iron and steel scrap. The impurities removed, however, depend on whether an acid (siliceous) or basic (limey) slag is used. An acid slag necessitates the use of an acid furnace lining (silica); a basic slag, a basic lining of magnesite or dolomite, with line in the charge. With an acid slag silicon, manganese and carbon only are removed by oxidation, consequently the raw material must not contain phosphorus and sulphur in amounts exceeding those permissible in the finished steel.
In the basic processes, silicon, manganese, carbon, phosphorus and sulphur can be removed from the charge, but normally the raw material contains low silicon and high phosphorus contents. To remove the phosphorus the bath of metal must be oxidised to a greater extent than in the corresponding acid process, and the final quality of the steel depends very largely on the degree of this oxidation, before deoxidisers-ferro-manganese, ferro-silicon, aluminium-remove the soluble iron oxide and form other insoluble oxides, which produce non-metallic inclusions if they are not removed from the melt:
2Al + 3FeO (soluble) « 3Fe + Al2O3 (solid)
In the acid processes, deoxidation can take place in the furnaces, leaving a reasonable time for the inclusions to rise into the slag and so be removed before casting. Whereas in the basic furnaces, deoxidation is rarely carried out in the presence of the slag, otherwise phosphorus would return to the metal. Deoxidation of the metal frequently takes place in the ladle, leaving only a short time for the deoxidation products to be removed. For these reasons acid steel is considered better than basic for certain purposes, such as large forging ingots and ball bearing steel. The introduction of vacuum degassing hastened the decline of the acid processes.
Bessemer steel
In both the Acid Bessemer and Basic Bessemer (or Thomas) processes molten pig iron is refined by blowing air through it in an egg-shaped vessel, known as a converter, of 15-25 tonnes capacity (Fig. 1). The oxidation of the impurities raises the charge to a suitable temperature; which is therefore dependent on the composition of the raw material for its heat: 2% silicon in the acid and 1,5-2% phosphorus in the basic process is normally necessary to supply the heat. The "blowing" of the charge, which causes an intense flame at the mouth of the converter, takes about 25 minutes and such a short interval makes exact control of the process a little difficult.
The Acid Bessemer suffered a decline in favour of the Acid Open Hearth steel process, mainly due to economic factors which in turn has been ousted by the basic electric arc furnace coupled with vacuum degassing.
The Basic Bessemer process is used a great deal on the Continent for making, from a very suitable pig iron, a cheap class of steel, e.g. ship plates, structural sections. For making steel castings a modification known as a Tropenas converter is used, in which the air impinges on the surface of the metal from side tuyeres instead of from the bottom. The raw material is usually melted in a cupola and weighed amounts charged into the converter.
In both the Acid Bessemer and Basic Bessemer (or Thomas) processes molten pig iron is refined by blowing air through it in an egg-shaped vessel, known as a converter, of 15-25 tonnes capacity (Fig. 1). The oxidation of the impurities raises the charge to a suitable temperature; which is therefore dependent on the composition of the raw material for its heat: 2% silicon in the acid and 1,5-2% phosphorus in the basic process is normally necessary to supply the heat. The "blowing" of the charge, which causes an intense flame at the mouth of the converter, takes about 25 minutes and such a short interval makes exact control of the process a little difficult.
The Acid Bessemer suffered a decline in favour of the Acid Open Hearth steel process, mainly due to economic factors which in turn has been ousted by the basic electric arc furnace coupled with vacuum degassing.
The Basic Bessemer process is used a great deal on the Continent for making, from a very suitable pig iron, a cheap class of steel, e.g. ship plates, structural sections. For making steel castings a modification known as a Tropenas converter is used, in which the air impinges on the surface of the metal from side tuyeres instead of from the bottom. The raw material is usually melted in a cupola and weighed amounts charged into the converter.
Open-hearth processes
In the Siemens process, both acid and basic, the necessary heat for melting and working the charge is supplied by oil or gas. But the gas and air are preheated by regenerators, two on each side of the furnace, alternatively heated by the waste gases. The regenerators are chambers filled with checker brickwork, brick and space alternating.
The furnaces have a saucer-like hearth, with a capacity which varies from 600 tonnes for fixed, to 200 tonnes for tilting furnaces (Fig. 1). The raw materials consist essentially of pig iron (cold or molten) and scrap, together with lime in the basic process. To promote the oxidation of the impurities iron ore is charged into the melt although increasing use is being made of oxygen lancing. The time for working a charge varies from about 6 to 14 hours, and control is therefore much easier than in the case of the Bessemer process.
The Basic Open Hearth process was used for the bulk of the cheaper grades of steel, but there is a growing tendency to replace the OH furnace by large arc furnaces using a single slag process especially for melting scrap and coupled with vacuum degassing in some cases.
In the Siemens process, both acid and basic, the necessary heat for melting and working the charge is supplied by oil or gas. But the gas and air are preheated by regenerators, two on each side of the furnace, alternatively heated by the waste gases. The regenerators are chambers filled with checker brickwork, brick and space alternating.
The furnaces have a saucer-like hearth, with a capacity which varies from 600 tonnes for fixed, to 200 tonnes for tilting furnaces (Fig. 1). The raw materials consist essentially of pig iron (cold or molten) and scrap, together with lime in the basic process. To promote the oxidation of the impurities iron ore is charged into the melt although increasing use is being made of oxygen lancing. The time for working a charge varies from about 6 to 14 hours, and control is therefore much easier than in the case of the Bessemer process.
The Basic Open Hearth process was used for the bulk of the cheaper grades of steel, but there is a growing tendency to replace the OH furnace by large arc furnaces using a single slag process especially for melting scrap and coupled with vacuum degassing in some cases.
Electric arc process
The heat required in this process is generated by electric arcs struck between carbon electrodes and the metal bath (Fig. 1). Usually, a charge of graded steel scrap is melted under an oxidising basic slag to remove the phosphorus. The impure slag is removed by tilting the furnace. A second limey slag is used to remove sulphur and to deoxidise the metal in the furnace. This results in a high degree of purification and high quality steel can be made, so long as gas absorption due to excessively high temperatures is avoided. This process is used extensively for making highly alloyed steel such as stainless, heat-resisting and high-speed steels.
Oxygen lancing is often used for removing carbon in the presence of chromium and enables scrap stainless steel to be used. The nitrogen content of steels made by the Bessemer and electric arc processes is about 0,01-0,25% compared with about 0,002-0,008% in open hearth steels.
The heat required in this process is generated by electric arcs struck between carbon electrodes and the metal bath (Fig. 1). Usually, a charge of graded steel scrap is melted under an oxidising basic slag to remove the phosphorus. The impure slag is removed by tilting the furnace. A second limey slag is used to remove sulphur and to deoxidise the metal in the furnace. This results in a high degree of purification and high quality steel can be made, so long as gas absorption due to excessively high temperatures is avoided. This process is used extensively for making highly alloyed steel such as stainless, heat-resisting and high-speed steels.
Oxygen lancing is often used for removing carbon in the presence of chromium and enables scrap stainless steel to be used. The nitrogen content of steels made by the Bessemer and electric arc processes is about 0,01-0,25% compared with about 0,002-0,008% in open hearth steels.
Oxygen processes
The high nitrogen content of Bessemer steel is a disadvantage for certain cold forming applications and continental works have, in recent years, developed modified processes in which oxygen replaces air. In Austria the LID process (Linz-Donawitz) converts low phosphorus pig iron into steel by top blowing with an oxygen lance using a basic lined vessel (Fig. 2b). To avoid excessive heat scrap or ore is added. High quality steel is produced with low hydrogen and nitrogen (0,002%). A further modification of the process is to add lime powder to the oxygen jet (OLP process) when higher phosphorus pig is used.